Crystal growth and characterization of two-leg spin ladder compounds: Sr14Cu24O41 and Sr2Ca12Cu24O41

Vanishri, S and Marin, C and Bhat, HL and Salce, B and Braithwaite, D and Regnault, LP (2009) Crystal growth and characterization of two-leg spin ladder compounds: Sr14Cu24O41 and Sr2Ca12Cu24O41. In: Journal of Crystal Growth, 311 (15). pp. 3830-3834.

[img] PDF
http___www.sciencedirect.com_science__ob=MImg&_imagekey=B6TJ6-4WMDHSY-7-K&_cdi=5302&_user=512776&_orig=search&_coverDate=07%2F15%2F2009&_sk=996889984&view=c&wchp=dGLzVtz-zSkWb&md5=44f67e658e3e.pdf - Published Version
Restricted to Registered users only

Download (282kB) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=ArticleUR...


Single crystals of Sr14−xCaxCu24O41 (x=0 and 12) are grown by the travelling solvent floating zone technique using an image furnace. The grown crystals are characterized for their single crystallinity by the X-ray and Neutron Laue method. The magnetic susceptibility measurements in Sr14Cu24O41 show considerable anisotropy along the main crystallographic axes. Low-temperature specific heat measurement and DC susceptibility measurement in Ca-doped crystal showed antiferromagnetic ordering at 2.8 K at ambient pressure. High-pressure AC susceptibility measurement on Ca-doped crystal showed a sharp superconducting transition at 2 K under 40 kbars. Tc onset reached a maximum value of 9.9 K at 54 kbars. The bulk superconductivity of the sample is confirmed by the high-pressure AC calorimetry with Tc max=9.4 K and TN=5 K at 56 kbars.

Item Type: Journal Article
Additional Information: Copyright of this article belongs to Elsevier Science.
Keywords: Floating zone technique;Single crystal growth;Travelling solvent zone growth;Cuprates;Oxide superconducting materials.
Department/Centre: Division of Physical & Mathematical Sciences > Physics
Depositing User: Id for Latest eprints
Date Deposited: 27 Oct 2009 12:22
Last Modified: 19 Sep 2010 05:45
URI: http://eprints.iisc.ac.in/id/eprint/23271

Actions (login required)

View Item View Item