Hot workability of as-cast Fe3Al-2.5%Cr intermetallic alloy

Sundar, RS and Sastry, DH and Prasad, YVRK (2003) Hot workability of as-cast Fe3Al-2.5%Cr intermetallic alloy. In: Materials Science and Engineering A, 347 (1-2). pp. 86-92.

[img] PDF
sdarticle30.pdf - Published Version
Restricted to Registered users only

Download (386kB) | Request a copy
Official URL: http://www.sciencedirect.com/science?_ob=ArticleUR...


Processing characteristics of as-cast Fe3Al-2.5%Cr alloy have been studied using constant strain rate isothermal compression tests in the temperature range 1023-1323 K and strain rate range 0.001-10 s(-1). At strain rates less than or equal to0.1 s(-1), the stress-strain curves are of steady-state type while at higher strain rates the flow stress reaches a peak before falling into either a steady-state or continuous flow softening with strain. The processing map of the alloy revealed a domain of dynamic recrystallization (DRX) at temperatures greater than 1123 K and the optimum conditions for processing occur at 1273 K and at strain rate of 0.001 s(-1) However, at higher temperatures, due to dynamic grain growth, the optimum condition for processing has moved to higher strain rates. Flow instabilities occur in the form of adiabatic shear bands when deformed at strain rates greater than 0.1 s(-1) and at temperatures less than or equal to1123 K. A constitutive relationship for hot working is developed to describe the relationship between flow stress, strain rate and temperature.

Item Type: Journal Article
Publication: Materials Science and Engineering A
Publisher: Elsevier Science
Additional Information: Copyright of this article belongs Elsevier Science.
Keywords: Intermetallics;Iron aluminides;Flow stress;High temperature deformation;Deformation mechanisms;Dynamic recrystallization; Constitutive relationship;Hot workability.
Department/Centre: Division of Mechanical Sciences > Materials Engineering (formerly Metallurgy)
Date Deposited: 12 Aug 2009 09:06
Last Modified: 19 Sep 2010 04:55
URI: http://eprints.iisc.ac.in/id/eprint/17031

Actions (login required)

View Item View Item